RODRIGUEZ RUIZ, Johana; PAJARO PAYARES, Adolfo and MEZA FUENTES, Edgardo. Synthesis and structural characterization of Zn-Al-Cu hydrotalcites. Rev.Colomb.Quim. [online]. 2016, vol.45, n.3, pp.33-38. ISSN 0120-2804. https://doi.org/10.15446/rev.colomb.quim.v45n3.61381.
Hydrotalcite-like compounds have been used in catalysis, medicine, environmental chemistry, and other applications. Depending on the metals present, the solids obtained by calcination can be used due to their basicity, memory effect, and high specific surface area. This study describes some characteristics of hydrotalcites based on Cu-Zn-Al. The solids were characterized by AAS, XRD, FTIR, DSC and TGA. In the FTIR spectra it was observed that in the solids with higher copper contents the band signed to O••H stretching (M••OH, H••OH) was moved to lower wave number values, because electron density of hydroxide groups orients toward the metallic copper center. In all materials hydrotalcite phase formation was observed and the Cu(OH)) phase in solids with higher copper content was detected, fact attributed to the Jahn-Teller effect. Results indicate that the collapse of the structure occurs at lower temperatures in the case of solids with higher copper content. In all the tested materials the decomposition of the HTLc structure and the formation ofmetal oxides was observed, as well as decomposition of carbonate ions occluded in the solid dueto the collapse of the lamellar structure.
Keywords : Hydrotalcite; copper; collapse of structure.