MEZA-FUENTES, Edgardo; RODRIGUEZ-RUIZ, Johana e RANGEL, Maria do Carmo. Characteristics of NiO present in solids obtained from hydrotalcites based on Ni/Al and Ni-Zn/Al. Dyna rev.fac.nac.minas [online]. 2019, vol.86, n.210, pp.58-65. ISSN 0012-7353. https://doi.org/10.15446/dyna.v86n210.78559.
NiO has a variety of applications, mainly in the production of electrochemical sensors and of metallic nickel. In addition, it is widely used as catalysts to produce hydrogen from natural gas. In this work, hydrotalcites based on nickel-aluminum and nickel-zinc-aluminum were synthesized, calcined at 500 °C and studied by different techniques. It was observed that nickel-aluminum hydrotalcites are thermally more stable, collapsing at higher temperatures than hydrotalcites containing zinc. During calcination, aluminum is incorporated into NiO lattice, leading to a decrease in crystallographic parameters. However, zinc decreases this effect, favoring the formation of NiO with lattice parameters close to pure nickel oxide. Zinc also contributes to the formation of smaller NiO particles, which is very useful for its use as a catalyst. In addition, aluminum led to a distortion in NiO lattice, an effect that is minimized by zinc, showing that it hinders the incorporation of Al3+ in the NiO lattice.
Palavras-chave : hidrotalcite; NiO; lattice parameters; spectroscopy Raman.